Aluminium A96351 and Aluminium Alloy A96351 Sheet or Plate

• Color: Silver
• Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations
• Certification: RoHS, ISO9001, ASTM, JIS, GB, EN, ASTMB
• Technique: Extruded
• Grade: 6000 Series
• Temper: T351 - T651
• Model NO.: 6351/AlSi1Mg0.5Mn/A96351
• Surface Treatment: Mill Finish
• Alloy: Alloy
• Form/Shape: Sheet,Plate,Bar,Rod,Tube,Pipe,Strip,Foil an
• Application-1: Is Chiefly Used to Manufacture
• Payment: T/T 30% Prepayment, 70% Balance Before Delivery
• Melting Point: 600-650
• Density: 2.7-2.8g/Cm³
• Transport Package: Standard Export Packaging
• Specification: 0.5-200mm*500-2500mm*500-100000mm
• Trademark: Taixie
• Origin: China
• HS Code: 7606910000
• Production Capacity: 10 Tons Per Month

Product Description

1.[aluminium  alloy 6351/AlSi1Mg0.5Mn/A96351] 
Introduction:

6351 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6351 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6351. A96351 is the UNS number. Additionally, the EN chemical designation is AlSi1Mg0,5Mn.

It originally received its standard designation in 1958.

The properties of 6351 aluminum include nine common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare 6351 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

6351-H111 Aluminum6351-O Aluminum
6351-T1 Aluminum6351-T11 Aluminum
6351-T4 Aluminum6351-T5 Aluminum
6351-T51 Aluminum6351-T54 Aluminum
6351-T6 Aluminum

Aluminum alloys tend to lose their strength when they are exposed to temperatures of about 200-250°C. However, their strength increases at subzero temperatures. They have high corrosion resistance.

2.[aluminium  alloy 6351/AlSi1Mg0.5Mn/A96351] 
Application:

The aluminum 6351 alloy is used in manufacturing tubes and pipes.

3.[aluminium  alloy 6351/AlSi1Mg0.5Mn/A96351] 
Chemistry:

Chemical Composition

The chemical composition of the aluminum 6351 alloy is tabulated below.

Element	Content (%)
Aluminum, Al	97.8
Silicon, Si	1
Manganese, Mn	0.6
Magnesium, Mg	0.6

Physical Properties

The following table shows the physical properties of the aluminum 6351 alloy.

Properties	Metric	Imperial
Density	2.6-2.8 g/cc	0.0939- 0.101 lb/in^3

Mechanical Properties

The mechanical properties of the aluminum 6351 alloy are outlined in the following table.

Properties	Metric	Imperial
Tensile strength	250 MPa	36260 psi
Yield strength	150 MPa	21756 psi
Shear strength	200 MPa	29008 psi
Fatigue strength	90 MPa	13054 psi
Elastic modulus	70-80 GPa	10153-11603 ksi
Poisson's ratio	0.033	0.033
Elongation	20%	20%
Hardness	95	95

Thermal Properties

The thermal properties of the aluminum 6351 alloy are given in the following table.

Properties	Conditions
T (ºC)	Treatment
Thermal conductivity	176 W/m-K	25	T6

4.[aluminium  alloy 6351/AlSi1Mg0.5Mn/A96351] 

Surface :

mill finish ,  not polished,
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled

5.[aluminium  alloy 6351/AlSi1Mg0.5Mn/A96351] 
Specification:

Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on 

Surface : Mill Finish(Not Polished ) ,polished  ,colour-coated, sand blasting  , brushed,mirror ,embossed ,oxidized,anodic oxidation    cold-rolled,hot-rolled  


6.These are our  warehouse  pictures:













7.These  are packaging  pictures :