Steel C60r 1.1223 Sheet or Plate for Project

• Customization: Available
• Standard: DIN, JIS, AISI, ASTM, GB, BS
• Technics: Cold Drawn
• Model NO.: C60R 1.1223
• Surface: Polished
• Alloy: Alloy
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Certification: RoHS, ISO9001, ASTM, JIS, GB, En, Astmb
• Technique: Cold Drawn
• Surface Treatment: Mill Finish(Not Polished)
• Form/Shape: Sheet, Plate, Bar, Rod, Tube, Pipe, Strip, Foil an
• Payment: T/T 30% Prepayment, 70% Balance Before Delivery
• Delivery Time: 2-5 Working Days After Getting The Prepayment
• Transport Package: Standard Export Packaging
• Specification: 0.5-200mm*500-2500mm*500-100000mm
• Trademark: Taixie
• Origin: China
• HS Code: 7606910000
• Production Capacity: 10 Tons Per Month

Product Description

1.[C60R 1.1223  sheet  or plate] 
Introduction:

 

Standard:

EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering     EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels     EN 10132-3: 2000 Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Steels for quenching and tempering     EN 10250-2: 2000 Open steel die forgings for general engineering purposes. Non-alloy quality and special steels     EN 10297-1: 2003 Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Technical delivery conditions

Equivalent grades of   steel   C60E (1.1221)
Warning! Only for reference

EU EN	Germany DIN,WNr	Japan JIS	France AFNOR	England BS	Italy UNI	Spain UNE	China GB	Russia GOST	Inter ISO
C60E	Ck60	S58C	XC60	070M60 CS60	C60	C55k	60	60 60G	C60E4

2.[C60R 1.1223   sheet or plate]

 Surface:

mill finish (not polished)
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled


3.[C60R 1.1223   sheet or plate] 
Chemistry:

Chemical composition %   of   steel   C60E (1.1221):   EN 10277-5-2008

Cr + Mo + Ni = 0.63

C	Si	Mn	Ni	P	S	Cr	Mo
0.57 - 0.65	max   0.4	0.6 - 0.9	max   0.4	max   0.03	max   0.035	max   0.4	max   0.1

 

 

Mechanical properties of   steel   C60E (1.1221)

Nominal thickness (mm):	to 16	16 - 100	100 - 250	250 - 500	500 - 1000
Rm - Tensile strength (MPa) (+N)	710	670	650	630	620

Nominal thickness (mm):	0.3 - 3
Rm - Tensile strength (MPa) (+A)	620

Nominal thickness (mm):	0.3 - 3
Rm - Tensile strength (MPa) (+QT)	1150-1750

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40
Rm - Tensile strength (MPa) (+C)	800-1150	780-1130	730-1100

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
Rm - Tensile strength (MPa) (+QT)	850	800	750	710

 

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
ReH - Minimum yield strength (MPa) (+QT)	580	520	450	420

 

Nominal thickness(mm):	to 16	16 - 100	100 - 250	250 - 500	500 - 1000
Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+N)	380-390	340-350	310	275	260

Nominal thickness(mm):	0.3 - 3
Rp0.2 0.2% proof strength (MPa) (+A)	495

Nominal thickness(mm):	5 - 10	10 - 16	16 - 40
Rp0.2 0.2% proof strength (MPa) (+C)	630	550	480

 

Nominal thickness (mm):	0.3 - 3
A - Min. elongation Lo = 80 mm (%) (+A)	17

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40
A - Min. elongation at fracture (%) (+C)	5	5	6

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
A - Min. elongation at fracture (%) longitud., (+QT)	11	13	14	14

 

Nominal thickness (mm):	to 16	16 - 100	100 - 250
A - Min. elongation Lo = 5,65 √ So (%) (+N)	10	11	11

 

Brinell hardness   (HBW):   (+S)	255
Brinell hardness   (HBW):   (+A)	241
Brinell hardness   (HBW):   (+SH)	198 - 278
Vickers hardness  ( HV):   (+A)	195
Vickers hardness  ( HV):   (+CR)	305
Vickers hardness  ( HV):   (+QT)	345 - 530

 