Alsi7mg0.3 Aluminum Aluminium Alloy for Castinge Nac - Alsi7mg0.3enac-42100 3.2371 Aluminum

• Shape: Round
• Application: Transportation Tools, Glass Wall, Heat Sink, Decorations
• Certification: ASTM
• Technique: Extruded
• Grade: 6000 Series
• Temper: O - H112
• Model NO.: AlSi7Mg0.3 aluminum Aluminium alloy for casting
• Surface Treatment: Color Coated
• Alloy: Alloy
• Transport Package: Wooden Box
• Specification: din 20-300
• Trademark: taixie
• Origin: Chian
• HS Code: 2501001100
• Production Capacity: 50000kgs

Product Description

AlSi7Mg0.3 aluminum

Aluminium alloy for casting

ENAC - AlSi7Mg0. 3

ENAC-42100

3.2371 Aluminum
 

EN AC-42100 (AISi7Mg0.3) cast aluminum

EN AC-42100 aluminium is an aluminium alloy formulated for casting. 42100 is the EN numeric name for this material. In addition, the chemical name of EN is AISi7Mg0, 3.

 

It has the highest electrical conductivity of European standard (EN) cast aluminium. In addition, it has a moderately high melting temperature and moderately high thermal conductivity.

 

The properties of EN AC-42100 aluminum include two common variations. This page shows a summary range for both. For more specific values, click on the link below. The chart bar on the Material Properties card below compares EN AC-42100 aluminum to: European Standard (EN) cast aluminum (top), all aluminum alloys (middle) and the entire database (bottom). The full bar line means that this is the maximum in the relevant set. A half-full bar means it's 50% of the top price, and so on.
 

Mechanical properties of AlSi7Mg0.3 aluminum:

 

Tensile strength σb (MPa) : ≥220

 

Yield strength σs (MPa) : ≥180

 

Elongation δ5 (%) : ≥2

 

Hardness (HB) : 65 -- 95

 

AlSi7Mg0.3 aluminum Heat treatment specification: quenching :535±5ºC, raised temperature 2h, up to 535ºC, hold for 8-12h, 65ºC water cooling, less than 45S, annealing, aging or tempering :180±5ºC, raised temperature 1h, hold for 4 ~ 8h; Then air cooling.

 

 

 

 

 

AlSi7Mg0.3 aluminum Chemical composition:

 

Silicon: 6.5 to 7.5

 

Magnesium Mg: 0.25 ~ 0.45

 

Aluminum Al: allowance

 

Iron (sand casting) : 0.000 ~ 0.500

 

Iron (metal casting) : 0.000 ~ 0.900

 

Copper Cu: ≤0.2(≤0.1 when used in the ocean)(impurity)

 

Manganese Mn: ≤0.35(impurity)

 

Zinc Zn: ≤0.3(impurity)

 

Ti+ Rare Earth Ti+Zr: ≤0.25(impurity)

 

Specification for heat treatment of AlSi7Mg0.3 aluminum:

 

Quenching :535±5ºC, increase temperature for 2h, rise to 535ºC, hold for 8-12h, water cooling at 65ºC, less than 45S, annealing, aging [1] or tempering :180±5ºC, increase temperature for 1h, hold for 4-8h; Then air cooling.

 

AlSi7Mg0.3 aluminum casting method:

 

Sand casting modification treatment, investment casting modification treatment, shell casting modification treatment (SB.RB.KB)

 

Beryllium Be: ≤0.1(impurity)

 

Tin Sn: ≤0.01(impurity)

 

Lead Pb: ≤0.05(impurity)

 

Yttrium Y: In order to improve mechanical properties, can contain 0.08 ~ 0.20, but Fe≤0.3

 

Note: total impurities :(sand casting)≤1.1; (metal casting)≤1.