Aluminium Alloy A93105 Sheet or Plate

• Customization: Available
• Color: Silver
• Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations
• Model NO.: A93105
• Certification: RoHS, ISO9001, ASTM, JIS, GB, EN, ASTMB
• Technique: Extruded
• Grade: 1000 Series
• Temper: O - H112
• Surface Treatment: Color Coated
• Alloy: Alloy
• Density: 2.70 g/cm3
• Melting Point: 630 - 655°c
• Transport Package: Standard Export Packaging
• Specification: 0.5-200mm*500-2500mm*500-100000mm
• Trademark: Taixie
• Origin: China
• HS Code: 7606910000
• Production Capacity: 10 Tons Per Month

Product Description

[aluminium  alloy A93105 sheet] 

Introduction:
 

Chemical Composition

The chemical composition of Aluminium / Aluminum A93105 alloy is tabulated below.

Element	Content (%)
Aluminium / Aluminum, Al	99.0
Manganese, Mn	0.55
Magnesium, Mg	0.50

Physical Properties

The following table shows the physical properties of Aluminium / Aluminum A93105 alloy.

Properties	Metric	Imperial
Density	2.6-2.8 g/cm^3	0.0939- 0.101 lb/in^3
Melting point	641°C	1185°F

Mechanical Properties

The mechanical properties of Aluminium / Aluminum A93105 alloy are outlined in the following table.

Properties	Metric	Imperial
Tensile strength	150 MPa	21755 psi
Yield strength	130 MPa	18855 psi
Shear strength	97 MPa	14069 psi
Elastic modulus	70-80 GPa	10153-11603 ksi
Poisson's ratio	0.33	0.33
Elongation	7%	7%

Thermal Properties

The thermal properties of Aluminium / Aluminum A93105 alloy are given in the following table.

Properties	Metric	Imperial
Thermal conductivity (@25°C/77°F)	173 W/mK	1201 BTU in/hr.ft².°F

Aluminium / Aluminum A93105 alloy has average machinability. However, its machinability can be increased in harder tempers than in annealed condition. Oil lubricants are used for machining this alloy.

Forming

Aluminium / Aluminum A93105 alloy has good forming characteristics. It is suggested that bend radii should be used in one thickness to 2 t range for annealed H12, H14 and H16 tempers. Bend radii of 2 to 7 t should be used for the H18 temper.

Welding

Aluminium / Aluminum A93105 alloy has good weldability. It can be welded using arc welding method.

Heat Treatment

Aluminium / Aluminum A93105 alloy does not react to heat treatment except during cold working.

Forging

Aluminium / Aluminum A93105 alloy can be forged at the temperatures ranging from 372 to 510°C (700 to 950°F).

Hot working

Aluminium / Aluminum A9 3105 alloy can be hot worked at 205 to 372°C (400 to 700°F)

Cold Working

Aluminium / Aluminum A93105 alloy has good cold working characteristics in the harder cold worked tempers.

Annealing

Aluminium / Aluminum A93105 alloy is annealed at 344°C (650°F) followed by cooling in air.

Hardening

Aluminium / Aluminum A93105 alloy can be hardened only by cold working in H12, 14, 16, 18 or 25 tempers.

[aluminium  alloy  A93105 sheet] 
Surface 

mill finish ,  Not Polished,brushed,mirror ,embossed ,oxidized,cold-rolled,hot-rolled 


[aluminium  alloy  A93105 sheet]
Specification:

Outside Diameter - 0.25mm (0.010") up to 16.00mm (0.625")
Wall - 0.05mm (0.002") up to 1.00mm (0.040")
Straight Lengths - 1.00mm (0.040") up to 5000.00mm (197")
Coils Lengths - 5 Metres to 15 Metres
Standard Tolerance- OD &ID +/-0.03mm (0.0012")
Wall +/- 10%
Tight Tolerance - OD&ID +/- 0.015mm (0.0006")
Wall +/-3%
Some thin wall tubes up to 25.40 mm (1.000") can be supplied.
 

[aluminium  alloy  A93105 sheet] 
Applications 

 

Aluminium / Aluminum A93105 alloy is used in sheet metal work. It is also used in manufacturing mobile homes, residential siding, and rain carrying goods.

[aluminium  alloy  A93105 sheet]  Picture:

This  is  sheet/plate : 





This  is bar/ rod:


This  is hexagonal rod:




This  is  pipe/tube : 




This  is packaging :



If  you want to know more information about aluminium  alloy A93105 sheet, please  send email  to us, we will contact you within one business day. We guarantee that your information will not be divulged to the third party.