5000 series aluminum alloys have very good corrosion resistance, weldability, workability, strength, and toughness.
Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres.
It has higher strength than 5251. This high strength makes Aluminium 5754 highly suited to flooring applications.
After rolling, Aluminium 5754 spontaneously softens until it reaches a stable condition.
[aluminium alloy A95754 / AlMg3/3.3535/ Al 3.1Mg Mn Cr ]
Application:
Aluminium 5754 is used in:
Table 1. Chemical composition for aluminium alloy 5754
| Element | % Present |
|---|---|
| Si | 0.4 |
| Fe | 0.4 |
| Mn | 0.5 |
| Mg | 2.6-3.2 |
| Al | Balance |
Table 2 (a). Mechanical properties for aluminium alloy 5754 H111 Treadplate
| BS EN 485-2:2008 Sheet 0.2mm to 6.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 60 Min MPa |
| Tensile Strength | 160 - 200 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 44 HB |
*Properties above are for material in the H111 condition.
Some thicknesses have a slightly higher minimum elongation requirement.
Table 2 (b). Mechanical properties for aluminium alloy 5754 H114
| BS EN 485-2:2008 Aluminium Sheet 0.2mm to 6.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 80 Min MPa |
| Tensile Strength | 190 - 260 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 52 HB |
*Properties above are for material in the H114 condition
Table 2 (c). Mechanical properties for aluminium alloy 5754 H22
| BS EN 485-2:2008 Sheet & Plate 0.2mm to 40mm |
|
|---|---|
| Property | Value |
| Proof Stress | 130 Min MPa |
| Tensile Strength | 220 - 270 MPa |
| Elongation A50 mm | 7 Min % |
| Hardness Brinell | 63 HB |
*Properties above are for material in the H22 condition.
Some thicknesses have a slightly higher minimum elongation requirement.
Table 2 (d). Mechanical properties for aluminium alloy 5754 H24
| BS EN 485-2:2008 Sheet & Plate 0.2mm to 25mm |
|
|---|---|
| Property | Value |
| Proof Stress | 160 Min MPa |
| Tensile Strength | 240 - 280 MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 70 HB |
*Properties above are for material in the H24 conditions.
Some thicknesses have a slightly higher minimum elongation requirement.
Table 2 (e). Mechanical properties for aluminium alloy 5754 H26
| BS EN 485-2:2008 Sheet 0.2mm to 6mm |
|
|---|---|
| Property | Value |
| Proof Stress | 190 Min MPa |
| Tensile Strength | 265 - 305 MPa |
| Elongation A50 mm | 4 Min % |
| Hardness Brinell | 78 HB |
*Properties above are for material in the H26 conditions.
Some thicknesses have a slightly higher minimum elongation requirement.
Table 3. Physical properties for aluminium alloy 5754
| Property | Value |
|---|---|
| Density | 2.66 kg/m3 |
| Melting Point | 600°C |
| Modulus of Elasticity | 68 GPa |
| Electrical Resistivity | 0.049x10-6 Ω.m |
| Thermal Conductivity | 147 W/m.K |
| Thermal Expansion | 24x10-6 /K |
Aluminium 5754 also corresponds to the following standard designations and specifications:
Aluminium 5754 has excellent weldability. The recommended filler alloy is 5356
Table 4. Fabrication response for aluminium alloy 5754
| Process | Rating |
|---|---|
| Workability - Cold | Very good |
| Machinability | Average |
| Weldability - Gas | Excellent |
| Weldability - Arc | Excellent |
| Weldability - Resistance | Excellent |
| Brazability | Poor |
| Solderability |
The most common tempers for 5754 aluminium are shown below with H111 being the most common treadplate temper