1.[ 41CrS4 1.7039 bar&rod ]
Introduction:
Standard: |
EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels |
EN 10263-4: 2001 Steel rod, bars and wire for cold heading and cold extrusion. Technical delivery conditions for steels for quenching and tempering |
EN 10250-3: 2000 Open steel die forgings for general engineering purposes. Alloy special steels |
EN 10297-1: 2003 Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Technical delivery conditions |
|
Equivalent grades of steel 41Cr4 (1.7035)
Warning! Only for reference
EU
EN |
Germany
DIN,WNr |
Japan
JIS |
France
AFNOR |
England
BS |
Italy
UNI |
Spain
UNE |
Russia
GOST |
Inter
ISO |
41Cr4 |
|
|
|
|
|
|
|
|
2.[41CrS4 1.7039 bar&rod ]
Surface:
mill finish (not polished)
brushed
mirror
embossed
oxidized
cold-rolled
hot-rolled
3.[41CrS4 1.7039 bar&rod ]
Chemistry:
Chemical composition % of steel 41Cr4 (1.7035): EN 10083-3-2006
C |
Si |
Mn |
P |
S |
Cr |
0.38 - 0.45 |
max 0.4 |
0.6 - 0.9 |
max 0.025 |
max 0.035 |
0.9 - 1.2 |
Mechanical properties of steel 41Cr4 (1.7035)
Nominal diameter (mm): |
to 16 |
16 - 40 |
40 - 100 |
Rm - Tensile strength (MPa) (+QT) |
1000-1200 |
900-1100 |
800-950 |
Rm - Tensile strength (MPa) (+AC+C+AC) |
610 |
Nominal thickness (mm): |
to 8 |
8 - 20 |
20 - 50 |
Rm - Tensile strength (MPa) (+QT) |
1000 |
900 |
800 |
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; |
to 16 |
16 - 40 |
40 - 100 |
Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+QT) |
800 |
660 |
560 |
KV - Impact energy (J) (+QT) |
+20°
30-35 |
KV - Impact energy (J) transverse, (+QT) |
+20°
22 |
Nominal thickness (mm): |
to 16 |
16 - 40 |
40 - 100 |
A - Min. elongation Lo = 5,65 √ So (%) (+QT), round products |
11 |
12 |
14 |
Nominal diameter (mm): or for flat products thickness: to 8; 8-20; 20-60; |
to 16 |
16 - 40 |
40 - 100 |
Z - Reduction in cross section on fracture (%) (+QT) |
30 |
35 |
40 |
Z - Reduction in cross section on fracture (%) (+AC+C+AC) |
60 |
Brinell hardness (HBW): (+S) |
255 |
Brinell hardness (HBW): (+A) |
241 |