Steel 35nicr6 1.5815 Sheet&Plate for General Engineering

• Customization: Available
• Standard: DIN, JIS, AISI, ASTM, GB, BS
• Technics: Cold Drawn
• Model NO.: 35NiCr6 1.5815
• Surface: Polished
• Alloy: Non-alloy
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Color: Silver
• Certification: RoHS, ISO9001, ASTM, JIS, GB, En, Astmb
• Technique: Cold Drawn
• Surface Treatment: Mill Finish(Not Polished)
• Form/Shape: Sheet, Plate, Bar, Rod, Tube, Pipe, Strip, Foil an
• Payment: T/T 30% Prepayment, 70% Balance Before Delivery
• Delivery Time: 2-5 Working Days After Getting The Prepayment
• Transport Package: Standard Export Packaging
• Specification: 0.5-200mm*500-2500mm*500-100000mm
• Trademark: Taixie
• Origin: China
• HS Code: 7606910000
• Production Capacity: 10 Tons Per Month

Product Description

1.[  35NiCr6  1.5815   sheet&plate ] 
 

Standard:

EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels

Equivalent grades of   steel   35NiCr6 (1.5815)
Warning! Only for reference

EU EN	Germany DIN,WNr
35NiCr6	35NiCr6

2.[ 35NiCr6  1.5815    sheet&plate ]

 Surface:

mill finish (not polished)
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled


3.[  35NiCr6  1.5815    sheet&plate ] 
Chemistry:

Chemical composition %   of   steel   35NiCr6 (1.5815):   EN 10083-3-2006

C	Si	Mn	Ni	P	S	Cr
0.3 - 0.37	max   0.4	0.6 - 0.9	1.2 - 1.6	max   0.025	max   0.025	0.9 - 1.1

Mechanical properties of   steel   35NiCr6 (1.5815)

Nominal diameter (mm):	to 16	16 - 40	40 - 100
Rm - Tensile strength (MPa) (+QT)	880-1080	880-1080	780-980

 

Nominal diameter(mm):   or for flat products thickness: to 8; 8-20; 20-60;	to 16	16 - 40	40 - 100
Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+QT)	740	740	640

 

Nominal thickness (mm):	to 16	16 - 40	40 - 100
A - Min. elongation Lo = 5,65 √ So (%) (+QT), round products	12	14	15

 

Nominal diameter (mm):     or for flat products thickness: to 8; 8-20; 20-60;	to 16	16 - 40	40 - 100
Z - Reduction in cross section on fracture (%) (+QT)	40	40	40

 

Brinell hardness   (HBW):   (+A)

223