1.[aluminium alloy 6360 /AlSiMgMn/A96360]
Introduction:
6360 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6360 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6360. AlSiMgMn is the EN chemical designation. And A96360 is the UNS number.
It received its standard designation in 2001, making it a fairly young material.
The properties of 6360 aluminum include four common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare 6360 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
6360-T4 Aluminum6360-T5 Aluminum
6360-T6 Aluminum
6360-T66 Aluminum
2.[aluminium alloy 6360 /AlSiMgMn/A96360]
Application:
3.[aluminium alloy 6360 /AlSiMgMn/A96360]
Chemistry:
Chemical composition % of grade ENAW-AlSiMgMn ( ENAW-6360 )
| Fe |
Si |
Mn |
Cr |
Ti |
Cu |
Mg |
Zn |
Others |
- |
| 0.1 - 0.3 |
0.35 - 0.8 |
0.02 - 0.15 |
max 0.05 |
max 0.1 |
max 0.15 |
0.25 - 0.45 |
max 0.1 |
each 0.05; total 0.15 |
Al - remainder |
Mechanical properties of grade ENAW-AlSiMgMn ( ENAW-6360 )
|
| Rm - Tensile strength (MPa) (T4) |
110 |
|
| Rm - Tensile strength (MPa) (T5) |
150 |
|
| Rm - Tensile strength (MPa) (T6) |
185 |
|
| Rp0.2 0.2% proof strength (MPa) (T4) |
50 |
|
| Rp0.2 0.2% proof strength (MPa) (T5) |
110-120 |
|
| Rp0.2 0.2% proof strength (MPa) (T6) |
140 |
|
| A - Min. elongation at fracture (%) (T4) |
16 |
|
| A - Min. elongation at fracture (%) (T5) |
8 |
|
| A - Min. elongation at fracture (%) (T6) |
8 |
|
| A - Min. elongation Lo = 50mm (%) (T4) |
14 |
|
| A - Min. elongation Lo = 50mm (%) (T5) |
6 |
|
| A - Min. elongation Lo = 50mm (%) (T6) |
6 |
| Brinell hardness (HBW): (T4) |
40 |
| Brinell hardness (HBW): (T5) |
50 |
| Brinell hardness (HBW): (T6) |
60 |
Properties ENAW-AlSiMgMn
| Intended to be contact with food - no; |
4.[aluminium alloy 6360 /AlSiMgMn/A96360]
Surface :
mill finish , not polished,
brushed
mirror
embossed
oxidized
cold-rolled
hot-rolled
5.[aluminium alloy 6360 /AlSiMgMn/A96360]
Specification:
Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on
Surface : Mill Finish(Not Polished ) ,polished ,colour-coated, sand blasting , brushed,mirror ,embossed ,oxidized,anodic oxidation cold-rolled,hot-rolled
| Standard: |
EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties |