[aluminium alloy 6110 /6110-T9/A96110/Almg0.9si0.9mncu]
Introduction:
6110 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. Cited properties are appropriate for the T9 temper. To achieve this temper, the metal is solution heat-treated, artificially aged, then strain hardened. 6110 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6110. A96110 is the UNS number.
It originally received its standard designation in 1979.
It has the highest tensile strength among the 6000-series alloys in the database.
The graph bars on the material properties cards below compare 6110 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
[aluminium alloy 6110 /6110-T9/A96110/Almg0.9si0.9mncu]
Application:
[aluminium alloy 6110 /6110-T9/A96110/Almg0.9si0.9mncu ]
Chemistry:
Chemical composition % of grade ENAW-AlMg0.9Si0.9MnCu ( ENAW-6110A )
| Fe |
Si |
Mn |
Cr |
Cu |
Mg |
Zn |
Others |
- |
| max 0.5 |
0.7 - 1.1 |
0.3 - 0.9 |
0.05 - 0.25 |
0.3 - 0.8 |
0.7 - 1.1 |
max 0.2 |
each 0.05; total 0.15 |
Ti+Zr < 0.2; Al - remainder |
Mechanical properties of grade ENAW-AlMg0.9Si0.9MnCu ( ENAW-6110A )
|
| Rm - Tensile strength (MPa) (T5) |
380 |
|
| Rm - Tensile strength (MPa) (T6) |
380-410 |
|
| Rm - Tensile strength (MPa) (T4) |
320 |
|
| Rp0.2 0.2% proof strength (MPa) (T5) |
360 |
|
| Rp0.2 0.2% proof strength (MPa) (T6) |
360-380 |
|
| Rp0.2 0.2% proof strength (MPa) (T4) |
220 |
|
| A - Min. elongation at fracture (%) (T5) |
10 |
|
| A - Min. elongation at fracture (%) (T6) |
10 |
|
| A - Min. elongation at fracture (%) (T4) |
16 |
|
| A - Min. elongation Lo = 50mm (%) (T5) |
8 |
|
| A - Min. elongation Lo = 50mm (%) (T6) |
8 |
|
| A - Min. elongation Lo = 50mm (%) (T4) |
14 |
| Brinell hardness (HBW): (T5) |
115 |
| Brinell hardness (HBW): (T6) |
120 |
| Brinell hardness (HBW): (T4) |
85 |
Properties ENAW-AlMg0.9Si0.9MnCu
| Intended to be contact with food - no; |
[aluminium alloy 6110 /6110-T9/A96110 /Almg0.9si0.9mncu]
Surface
mill finish , not polished,
brushed
mirror
embossed
oxidized
cold-rolled
hot-rolled
[aluminium alloy 6110 /6110-T9/A96110 /Almg0.9si0.9mncu]
Specification:
Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on
Surface : Mill Finish(Not Polished ) ,polished ,colour-coated, sand blasting , brushed,mirror ,embossed ,oxidized,anodic oxidation cold-rolled,hot-rolled