6070 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6070 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6070. A96070 is the UNS number.
It originally received its standard designation in 1962.
The properties of 6070 aluminum include two common variations. This page shows summary ranges across both of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare 6070 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
is used in manufacturing pipelines and heavy duty welded structures.
The chemical composition of aluminium / aluminum 6070 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Aluminium / aluminum, Al | 97 |
| Silicon, Si | 1.40 |
| Magnesium, Mg | 0.80 |
| Manganese, Mn | 0.70 |
| Copper, Cu | 0.28 |
The physical properties of aluminium / aluminum 6070 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939- 0.101 lb/in3 |
The mechanical properties of aluminium / aluminum 6070 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 145 MPa | 21031 psi |
| Yield strength | 69 MPa | 10008 psi |
| Shear strength | 97 MPa | 14069 psi |
| Fatigue strength | 62 MPa | 8993 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 20% | 20% |
| Hardness | 35 | 35 |
The thermal properties of the aluminium / aluminum 6070 alloy are given in the following table.
| Properties | Conditions | ||
|---|---|---|---|
| Temp | Treatment | ||
| Thermal conductivity | 175 W/mK | 25ºC/77ºF | T6 |
| Element | Weight % |
| Al | 96.8 |
| Si | 1.40 |
| Cu | 0.28 |
| Mn | 0.7 |
| Mg | 0.80 |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 2.6-2.8 | 25 | |
| Poisson's Ratio | 0.33 | 25 | |
| Elastic Modulus (GPa) | 70-80 | 25 | |
| Tensile Strength (Mpa) | 145 | 25 | O more |
| Yield Strength (Mpa) | 69 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | |||
| Hardness (HB500) | 35 | 25 | O more |
| Shear Strength (MPa) | 97 | 25 | O more |
| Fatigue Strength (MPa) | 62 | 25 | O more |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Conductivity (W/m-K) | 172 | 25 | T6 |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Electric Resistivity (10-9W-m) | 39 | 25 | T6 |