Steel 34CrNiMo6V 1.6582 4340 Sncm447 Bar& Rod for General Engineering

• Standard: DIN, JIS, AISI, ASTM, GB, BS
• Technics: Hot Rolled
• Application: Structural Steel Bar
• Surface: Polished
• Alloy: Non-alloy
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Model NO.: 34CrNiMo6V 1.6582 4340 SNCM447
• Certification: RoHS, ISO9001, ASTM, JIS, GB, En, Astmb
• Technique: Cold Drawn
• Surface Treatment: Mill Finish(Not Polished)
• Form/Shape: Sheet, Plate, Bar, Rod, Tube, Pipe, Strip, Foil an
• Payment: T/T 30% Prepayment, 70% Balance Before Delivery
• Delivery Time: 2-5 Working Days After Getting The Prepayment
• Transport Package: Standard Export Packaging
• Specification: 0.5-200mm*500-2500mm*500-100000mm
• Trademark: Taixie
• Origin: China
• HS Code: 7606910000
• Production Capacity: 10 Tons Per Month

Product Description

1.[ Steel 36CrNiMo4 1.6511  Gr.9840 SCNM439   bar& rod ] 
Introduction:

 

Standard:

EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering     EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels     EN 10269: 1999 Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties     EN 10263-4: 2001 Steel rod, bars and wire for cold heading and cold extrusion. Technical delivery conditions for steels for quenching and tempering     EN 10250-3: 2000 Open steel die forgings for general engineering purposes. Alloy special steels

Equivalent grades of   steel   34CrNiMo6 (1.6582)
Warning! Only for reference

EU
EN

USA
-

Germany
DIN,WNr

Japan
JIS

France
AFNOR

England
BS

Italy
UNI

China
GB

Sweden
SS

Poland
PN

Czechia
CSN

Russia
GOST

Inter
ISO

34CrNiMo6

4340

34CrNiMo6

GS-34CrNiMo6V

SNCM447

35NCD6

817M40

35CrNiMo6

35NiCrMo6KB

34CrNi3Mo

34CrNiMo

ZG34CrNiMo

2541

34HNM

16342

16343

16444

36KH2N2MFA

38KH2N2MA

40KHN2MA

36CrNiMo6Equivalent grades of   steel   34CrNiMo6 (1.6582)
Warning! Only for reference

EU EN

USA -

Germany DIN,WNr

Japan JIS

France AFNOR

England BS

Italy UNI

China GB

Sweden SS

Poland PN

Czechia CSN

Russia GOST

Inter ISO

34CrNiMo6

4340

34CrNiMo6 GS-34CrNiMo6V

SNCM447

35NCD6

817M40

35CrNiMo6 35NiCrMo6KB

34CrNi3Mo 34CrNiMo ZG34CrNiMo

2541

34HNM

16342 16343 16444

36KH2N2MFA 38KH2N2MA 40KHN2MA

36CrNiMo6

2.[Steel 36CrNiMo4 1.6511  Gr.9840 SCNM439     bar& rod ]

 Surface:

mill finish (not polished)
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled


3.[Steel 36CrNiMo4 1.6511  Gr.9840 SCNM439   bar& rod ] 
Chemistry:

 

Chemical composition %   of   steel   34CrNiMo6 (1.6582):   EN 10277-5-2008

C	Si	Mn	Ni	P	S	Cr	Mo
0.3 - 0.38	max   0.4	0.5 - 0.8	1.3 - 1.7	max   0.025	max   0.035	1.3 - 1.7	0.15 - 0.3

 

Information for steel and alloy suppliers

Contact	Buying Requirements, Buying Leads   of   steel   34CrNiMo6 (1.6582)	Time
Country: India More info	Quantity: After SAMPLE APPROVAL Shape: Rod/Bar/Rebar	2020-02-02

Mechanical properties of   steel   34CrNiMo6 (1.6582)

Nominal diameter (mm):	to 16	16 - 40	40 - 100	100 - 160	160 - 250
Rm - Tensile strength (MPa) (+QT)	1200-1400	1100-1300	1000-1200	900-1100	800-950

Rm - Tensile strength (MPa) (+AC)	720

 

Nominal diameter(mm):   or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;	to 16	16 - 40	40 - 100	100 - 160	160 - 250
Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+QT)	1000	900	800	700	600

Nominal thickness(mm):	to 160	160 - 330	330 - 660
Re - Upper yield strength (MPa) (+QT)	600	540	490

 

KV - Impact energy (J) longitud., (+QT)	+20° 45	-40° 40

 

A - Min. elongation at fracture (%) transverse, (+QT)	9-14

 

Nominal thickness (mm):	to 16	16 - 40	40 - 100	100 - 160	160 - 250
A - Min. elongation Lo = 5,65 √ So (%) (+QT), round products	9	10	11	12	13

 

Nominal diameter (mm):     or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;	to 16	16 - 40	40 - 100	100 - 160	160 - 250
Z - Reduction in cross section on fracture (%) (+QT)	40	45	50	55	55

Z - Reduction in cross section on fracture (%) (+AC)	58

 

Brinell hardness   (HBW):   (+A)

248 - 255